Bambu PA6-GF - Glass Fiber Reinforced Nylon

Bambu PA6-GF, also known as Nylon 6 with Glass Fiber, stands at the forefront of high-performance engineering plastics. Engineered to deliver exceptional strength, durability, dimensional stability. The PA6-GF is also more cost effective when compared to other top tier engineering filaments.

Built to Last

Bambu PA6-GF is exceptionally strong and durable due to reinforced glass fibers, making it the perfect choice for prints that need to withstand heavy use and resist bending or breaking.

Dimensional Stability

PA6-GF boasts unparalleled dimensional stability thanks to its glass fiber reinforcement, minimizing warping in comparison to standard PA filaments. Print with precise dimensions, even in the most intricate geometries.

Exceptional Thermal Properties

PA6-GF boasts a high heat deflection temperature and superior dimensional stability, enabling it to retain its mechanical properties even under elevated temperatures. This makes it ideal for demanding industrial and automotive applications.

Chemical Resistance

PA6-GF offers excellent resistance to chemicals, oils, and many kinds of solvents, ensuring long-term performance in challenging environments.

Smooth Surface and More Colors

Bambu PA6-GF filaments are compatible with the Bambu AMS system, ready to print in multi-color. The special surface texture also blurs the layer lines, providing a smooth surface quality.

Product Features

Built to Last
Dimensional Stability
Exceptional Thermal Properties
Chemical Resistance
Smooth Surface and More Colors
Diameter: 1.75mm +/- 0.03mm

Cautions for Use

0.2 mm Nozzle Not Compatible
Stainless Steel Nozzle Not Recommended
AMS Compatible
AMS lite NOT Compatible
Dry before Use

Recommended Printing Settings

Recommended Printing Settings
Drying Settings before Printing	80 °C, 8 - 12 h
Printing and Keeping Container's Humidity	< 20% RH (Sealed, with Desiccant)
Nozzle Temperature	260 - 290 °C
Bed Temperature (with Glue)	80 - 100 °C
Printing Speed	< 130 mm/s

Physical Properties

Physical Properties
Density	1.14 g/cm³
Vicat Softening Temperature	210 °C
Heat Deflection Temperature	182 °C
Melting Temperature	219 °C
Melt Index	9.0 ± 0.8 g/10 min

Mechanical Properties

Mechanical Properties
Tensile Strength	75 ± 6 MPa
Breaking Elongation Rate	3.9 ± 0.8 %
Bending Modulus	3670 ± 140 MPa
Bending Strength	120 ± 6 MPa
Impact Strength	27.2 ± 2.2 kJ/m²